C11N-HS High-Strength Nano Insulation Sheet

C11N-HS is a rigid nanoporous insulation material primarily composed of fumed silica, reinforced with fibers and light‑blocking agents. It features mesopores smaller than 50 nm in diameter and effectively inhibits heat conduction, radiation, and convection, withstanding temperatures up to 1300°C.

Product Inquiry

Home page

Product Details

C11N-HS It is a rigid nanoporous insulation material, primarily composed of fumed silica, compounded with reinforcing fibers and light-shielding agents, with a mesopore diameter of less than 50nm , while simultaneously blocking heat conduction, heat radiation, and heat convection, with temperature resistance up to 1300℃ 。

Product features: Excellent high-temperature insulation performance, high resistance Compressive strength, can withstand 25MPa Pressure, Low compressive strain 。

Application areas: It is suitable for fire protection and thermal insulation of new‑type batteries in the new energy sector, as well as for thermal insulation applications involving high‑temperature equipment that must withstand mechanical loads, vibration, or impact.

Technical Specifications

Performance Name	Unit	Performance value	Test Standards and Methods
Thickness	mm	1.0~5.0	Thickness gauge
Core material density	kg/m3	420-540	Geometric Method Testing
Combustion performance	/	Non-flammable	GB 8624-2012
Thermal conductivity @25℃	W/(m·K)	≤0.038	GB/T 10295‑2008
Thermal conductivity @300℃		≤0.044
Thermal conductivity @500℃		≤0.048
Thermal conductivity @800℃		≤0.055
Fire Resistance Test Evaluation ( Butane torch 30min)	/	Flameless and non-penetrating	Butane torch ablation 30min
Compressive strength	MPa	CS(10)≥1	GB/T 134802014
		CS(20)≥5
		CS(30)≥9
		CS(40)≥20
Prohibited substances	/	Qualified	ROHS2.0
		Qualified	REACH
		Qualified	ELV
Performance Name	Unit	Performance value	Test Standards and Methods
Thickness	mm	1.0~5.0	Thickness gauge
Core material density	kg/m3	420-540	Geometric Method Testing
Combustion performance	/	Non-flammable	GB 8624-2012
Thermal conductivity @25℃	W/(m·K)	≤0.038	GB/T 10295‑2008
Thermal conductivity @300℃		≤0.044
Thermal conductivity @500℃		≤0.048
Thermal conductivity @800℃		≤0.055
Fire Resistance Test Evaluation ( Butane torch 30min)	/	Flameless and non-penetrating	Butane torch ablation 30min
Compressive strength	MPa	CS(10)≥1	GB/T 134802014
		CS(20)≥5
		CS(30)≥9
		CS(40)≥20
Prohibited substances	/	Qualified	ROHS2.0
		Qualified	REACH
		Qualified	ELV

Key Performance

3mm Compressive stress of the product - Stress-Strain Curve

Compression Performance:

Inlet pressure 0.001MPa , loading speed 2mm/min

Keywords:C11N-HS High-Strength Nano Insulation Sheet